Product details
Product Name: Polyamide 610 resin
We are a Polyamide 610 resin manufacture, based in Zibo ,China, specialized in Polyamide/Nylon Resin and Compounding with Annual Capacity of 20,000MT.
Product Information
The comprehensive performance of Polyamide 610 resin is stability; it has a great advantage in the field which has extreme requirements of water absorption and heat resistance. It's also can be used for injection molding and other extrusion applications.
Polyamide 610 resin is made through poly-condensation of hexamethylene diamine and sebacic acid.Sebacic acid is obtained from castor oil, so PA 610 is made as Bio-Based renewable materials.
Special features
● 63 % Bio-Based Carbon Content (as a fraction of total organic carbon)
● Low water absorption and good dimensional stability
● Good oil and alkali resistance
● High toughness and strength
● Excellent mould ability
PRODUCT SPECIFICATIONS
Test Items |
Test Methods |
Test Conditions |
Unit |
Typical Value |
|
Physical Properties | ||||
Density |
ISO 1183 |
23℃ |
Kg/m3 |
1075 |
|
Shore D Hardness |
ISO 868 |
— |
— |
80 |
|
Melting Range |
ISO 3146 |
— |
℃ |
210-230 |
|
Mechanical Properties | ||||
|
Tensile Strength |
ISO 527 |
50mm/min |
MPa |
55 |
|
Flexural Strength |
ISO 178 |
2mm/min |
MPa |
55 |
|
Charpy Impact Strength |
ISO 179/1eU |
23℃ |
KJ/m2 |
N |
|
Charpy Notched Impact Strength |
ISO 179/1eA |
23℃ |
KJ/m2 |
4.5 |
|
Other Properties | ||||
|
Water Absorption |
Sim.to.ISO 62 |
— |
% |
3.3 |
Typical Processing Conditions Drying Temperature: 80-100 ℃
Drying Time: 4-8 h
Injection Temperature: 240-260 ℃
Extrusion Temperature: 230-260 ℃
We can also provide POLYAMIDE 610 RESIN with different Viscosity as follows
● Low viscosity：<2.35------F120,
● Medium viscosity：2.35-2.75--- F150,
● High viscosity: > 2.75----F170.
Applications
Due to its stability and high melting point, POLYAMIDE 610 RESIN can be widely used in machinery manufacturing, making parts for automobile pipes, quick connectors, oil storage tank, textile machinery. It can also be used to make battery cell case and instruments rack in electronics and toothbrush fiber, monofilament and cable coating.